涂層測厚儀涂鍍層測試方法表
|
|
|
作者：峰志儀器 轉(zhuǎn)載自： 發(fā)布日期：2006-11-9
|
|
涂層測厚儀涂鍍層測試方法表……不同基材－涂鍍層(表1）
|
涂鍍層
基材
|
鋁
|
鉛
|
鉻
|
鋁氧化
磷化層
鉻酸鹽
|
瓷釉
油漆
塑料
|
金
|
鎘
|
銅
|
焊錫
焊接金屬
|
|
鋁及鋁合金
|
*
|
B,Q,X
|
B,E,Q,X
|
E
|
B,E
|
B,Q,X
|
B,Q,X
|
B,Q,X
|
B,X
|
|
玻璃、陶瓷、塑料
|
B,E,Q
|
B,X
|
B,Q,X
|
-
|
*
|
B,X
|
B,Q,X
|
B,E,Q,X
|
B,Q,X
|
|
金
|
-
|
-
|
B,Q,X
|
-
|
B
|
*
|
-
|
-
|
-
|
|
硬金屬：鎢、鉬
|
B,Q,X
|
X
|
B,X
|
-
|
B
|
X
|
(B),X
|
B,X
|
X
|
|
銅和銅合金
|
B, X
|
B,Q,X
|
E,Q,X
|
E
|
B,E
|
B,X
|
B,Q,X
|
(Q,X)
|
B,Q,X
|
|
鎂和鎂合金
|
*
|
B,X
|
B,E,X
|
E
|
B,E
|
B,X
|
B,X
|
B,X
|
B,X
|
|
鎳
|
B,Q,X
|
B,Q,X
|
B,Q,X
|
-
|
B,E
|
B,X
|
B,Q,X
|
Q,X
|
B,Q,X
|
|
銀
|
-
|
-
|
-
|
-
|
B,E
|
B,X
|
-
|
-
|
-
|
|
鐵和鋼
|
B,M,Q,X
|
B,M,Q,X
|
M,Q,X
|
M
|
B,M
|
B,M,X
|
B,M,Q,X
|
M,Q,X
|
B,M,Q,X
|
|
非磁性鋼
|
B,Q,X
|
B,Q,X
|
Q,X
|
-
|
B,E
|
B,X
|
B,Q,X
|
Q,X
|
B,Q,X
|
|
鈦和鈦合金
|
X
|
B,X
|
X
|
E
|
B,E
|
B,X
|
B,X
|
B,Q,X
|
B,Q,X
|
|
鋅和鋅合金
|
B,X
|
B,X
|
E,X
|
E
|
B,E
|
B,X
|
B,X
|
Q,X
|
B,X
|
測試方法表……不同基材－涂鍍層(表2）
|
涂鍍層
基材
|
黃銅
|
磁性鎳
|
非磁性鎳
|
鈀
|
PVD
CVD
|
鐒
|
銀
|
鋅
|
錫
|
|
鋁及鋁合金
|
B,N,Q,X
|
B,Q,X
|
B,X
|
B,Q,X
|
X
|
B,X
|
B,Q,X
|
B,Q,X
|
B,Q,X
|
|
玻璃、陶瓷、塑料
|
B,X
|
B,N,Q,X
|
B,Q,X
|
B,X
|
B,X
|
B,X
|
B,Q,X
|
B,Q,X
|
B,Q,X
|
|
金
|
-
|
-
|
-
|
B,X
|
-
|
B,X
|
B,X
|
-
|
-
|
|
硬金屬：鎢、鉬
|
B,X
|
B,N,X
|
X
|
(B),X
|
(B),X
|
(B),X
|
(B),X
|
B,X
|
B,X
|
|
銅和銅合金
|
X
|
N,Q,X
|
B,X
|
B,X
|
B,X
|
B,X
|
B,Q,X
|
B,X
|
B,X
|
|
鎂和鎂合金
|
B,X
|
B,N,X
|
B,X
|
B,X
|
X
|
B,X
|
B,X
|
B,X
|
B,X
|
|
鎳
|
X
|
*
|
B,X
|
B,X
|
B,X
|
B,X
|
B,Q,X
|
B,X
|
B,Q,X
|
|
銀
|
-
|
-
|
B,X
|
X
|
-
|
X
|
*
|
-
|
-
|
|
鐵和鋼
|
M,Q,X
|
(N),Q,X
|
B,M,X
|
B,M,X
|
B,M,X
|
B,X
|
B,M,Q,X
|
M,Q,X
|
B,M,Q,X
|
|
非磁性鋼
|
Q,X
|
N,Q,X
|
B,X
|
B,X
|
B,X
|
B,X
|
B,Q,X
|
Q,X
|
B,Q,X
|
|
鈦和鈦合金
|
B,X
|
B,N,X
|
B,X
|
B,X
|
*
|
B,X
|
B,X
|
B,X
|
B,X
|
|
鋅和鋅合金
|
X
|
N,X
|
B,X
|
B,X
|
B,X
|
B,X
|
B,X
|
*
|
B,X
|
符號說明：
|
E
|
渦流法
|
X
|
X－射線熒光法
|
*
|
不能測量
|
|
M
|
磁感應(yīng)法
|
B
|
β－射線反射法
|
-
|
極少遇見
|
|
N
|
改進磁感應(yīng)法
|
Q
|
庫侖法
|
( )
|
有限適用
|
|
|
|
|
|
|
|
 |
| |